document 599-1 document 599-1 revised 09/03/15 smt power inductors C mss1260t dcr 3 srf i sat (a) 5 i rms (a) 6 inductance 2 (mohms) typ 4 10% 20% 30% 20c 40c part number 1 (h) typ max (mhz) drop drop drop rise rise mss1260t-102nl_ 1.0 30% 5.8 6.5 100 19.12 21.18 22.76 6.00 8.00 mss1260t-152nl_ 1.5 30% 8.8 9.8 80.0 14.44 16.40 17.64 5.30 7.60 mss1260t-222nl_ 2.2 30% 11.5 12.8 55.0 12.32 14.00 15.08 5.20 7.30 mss1260t-332nl_ 3.3 30% 12.6 14.0 42.0 10.88 12.22 13.12 5.00 7.00 mss1260t-472ml_ 4.7 20% 13.9 15.5 38.0 9.92 11.10 12.00 4.50 7.00 mss1260t-562ml_ 5.6 20% 14.9 16.6 30.0 8.54 9.60 10.38 4.00 6.40 mss1260t-682ml_ 6.8 20% 16.6 18.5 27.0 7.80 8.80 9.44 3.80 5.90 mss1260t-822ml_ 8.2 20% 17.0 20.0 26.0 6.44 7.38 7.98 3.40 4.80 mss1260t-103ml_ 10 20% 21.5 23.9 22.0 6.00 6.92 7.48 3.00 4.00 mss1260t-123ml_ 12 20% 24.5 27.3 20.0 5.68 6.56 7.08 2.80 3.70 mss1260t-153ml_ 15 20% 27.0 32.0 18.0 5.34 6.04 6.54 2.60 3.50 mss1260t-183ml_ 18 20% 30.0 33.0 16.0 4.82 5.54 6.00 2.50 3.30 mss1260t-223ml_ 22 20% 36.6 40.7 15.0 4.42 5.04 5.44 2.30 3.10 mss1260t-273ml_ 27 20% 48.0 52.0 13.0 3.78 4.32 4.68 2.10 2.90 mss1260t-333ml_ 33 20% 54.0 57.0 12.4 3.50 4.00 4.34 2.00 2.70 mss1260t-393ml_ 39 20% 58.0 64.5 12.0 3.32 3.80 4.14 1.90 2.60 mss1260t-473ml_ 47 20% 75.0 82.0 11.6 2.84 3.26 3.54 1.85 2.50 mss1260t-563ml_ 56 20% 85.0 89.0 10.5 2.64 3.04 3.28 1.75 2.40 mss1260t-683ml_ 68 20% 94.5 105 10.0 2.46 2.82 3.04 1.70 2.30 mss1260t-823ml_ 82 20% 120 129 8.6 2.24 2.54 2.74 1.60 2.20 mss1260t-104ml_ 100 20% 139 146 7.8 2.06 2.34 2.54 1.50 2.10 mss1260t-124kl_ 120 10% 193 195 6.8 1.84 2.08 2.28 1.38 1.85 mss1260t-154kl_ 150 10% 209 216 6.4 1.64 1.90 2.06 1.20 1.66 mss1260t-184kl_ 180 10% 234 246 6.1 1.46 1.70 1.84 1.14 1.58 mss1260t-224kl_ 220 10% 306 335 5.5 1.30 1.48 1.60 1.00 1.42 mss1260t-274kl_ 270 10% 349 355 4.3 1.18 1.38 1.48 0.90 1.45 mss1260t-334kl_ 330 10% 482 494 4.0 1.04 1.20 1.30 0.84 1.16 mss1260t-394kl_ 390 10% 515 533 3.6 1.00 1.16 1.28 0.78 1.08 mss1260t-474kl_ 470 10% 705 733 3.0 0.906 1.00 1.10 0.70 0.96 mss1260t-564kl_ 560 10% 776 800 2.8 0.872 0.980 1.02 0.64 0.88 mss1260t-684kl_ 680 10% 887 910 2.6 0.782 0.886 0.956 0.58 0.80 mss1260t-824kl_ 820 10% 1130 1152 2.5 0.692 0.784 0.854 0.53 0.73 mss1260t-105kl_ 1000 10% 1295 1335 2.4 0.588 0.672 0.726 0.48 0.68 designers kit c418 contains 3 each of all values core material ferrite core and winding loss see www.coilcraft.com/coreloss terminations rohs compliant matte tin over nickel over phos bronze. other terminations available at additional cost. weight: 2.8 g C 3.3 g ambient temperature C40c to +125c with (40c rise) i rms current. maximum part temperature +165c (ambient + temp rise). derating . storage temperature component: C40c to +165c. tape and reel packaging: C40c to +80c resistance to soldering heat max three 40 second refows at +260c, parts cooled to room temperature between cycles moisture sensitivity level (msl) 1 (unlimited foor life at <30c / 85% relative humidity) failures in time (fit) / mean time between failures (mtbf) 38 per billion hours / 26,315,789 hours, calculated per telcordia sr-332 packaging 500/13 reel; plastic tape: 24 mm wide, 0.35 mm thick, 16 mm pocket spacing, 6.6 mm pocket depth pcb washing tested to mil-std-202 method 215 plus an additional aqueous wash. see doc787_pcb_washing.pdf . ? designed for high ambient temperatures C 125c ? magnetic shielding, very low dcr, excellent current handling 1. please specify termination and packaging codes: mss1260t-105k ld termination: l = rohs compliant matte tin over nickel over phos bronze. special order: t = rohs tin-silver-copper (95.5/4/0.5) or s = non-rohs tin-lead (63/37). packaging: d = 13 machine-ready reel. eia-481 embossed plastic tape (500 parts per full reel). b = less than full reel. in tape, but not machine ready. to have a leader and trailer added ($25 charge), use code letter d instead. 2. inductance tested at 100 khz, 0.1 vrms, 0 adc using an agilent/hp 4263b lcr meter or equivalent. 3. dcr measured on a micro-ohmmeter and a coilcraft ccf858 test fxture. 4. srf measured using an agilent/hp 8753d network analyzer and a coilcraft smd - d test fxture. 5. dc current at 25c that causes the specifed inductance drop from its value without current. click for temperature derating information . 6. current that causes the specifed temperature rise from 25c ambient. this information is for reference only and does not represent absolute maximum ratings. click for temperature derating information . 7. electrical specifcations at 25c. refer to doc 362 soldering surface mount compo - nents before soldering. high tempera ture
document 599-2 document 599-2 revised 09/03/15 smt power inductors C mss1260t series 1 0. 1 10 100 1000 10000 0.1 1 100 10 inductance (h) current (a) 1 h 100 h 10 h 1000 h 0.217 5,5 recommende d land pattern 0.157 4,0 for optional tin-lead and tin-silver-copper terminations, dimensions are for the mounted part. dimensions before mounting can be an additional 0.012 inch (0,3 mm). 0.334 8,5 0.24 0.008 6,0 0,2 0.025 0,635 * * * parts m anufactured p rior to a ugust 2011 ma y h ave a d ifferent p art m arking. 0.197 0.008 5,0 0,2 0.197 0.016 5,0 0,4 0.138 0.016 3,5 0,4 0.472 0.012 12,0 0,3 0.472 0.012 12,0 0,3 123 x internal code dash number typical l vs frequency typical l vs current 1 0. 1 10 100 1000 10000 0.01 0.1 10 1 inductance (h) frequency (mhz) 1 h 100 h 10 h 1000 h dimensions are in inches mm high tempera ture
|